1.7035 / 41Cr4
DIN 1.7035 / 41Cr4 Steel is one of the most widely used alloy steel. After QT heat treatment,41Cr4 steel has good comprehensive mechanical properties,low temperature impact toughness and hardenability. DIN 1.7035 steel can get higher fatigue strength after oil cooling. The machinability of 41Cr4 steel is good for normalizing and QT condition. But the weldability of 1.7035 alloy steel is not so good that it’s easy to produce cracks. This material requires preheating before welding.
C: 0.38-0.45; Si: max0.40; Mn: 0.60-0.90;
P: max0.025; S: max0.035; Cr: 0.90-1.20;
Form of 1.7035
Round / Square / Flat Bars, Shafts, Rollers, Blocks
Size of 41Cr4
– As Forged
(Forged Flat Bars, Shafts, Rollers and Blocks can be Customized)
– As Rolled
Length: 3,000-10,000mm(can be Customized)
Surface Condition of 1.7035 Steel
Black, Rough Machined, Turned
Hardness of 41Cr4 Steel
Annealed (+A): max 207HB
Treated to improve shearability (+S): max 255HB
Mechanical Properties of 1.7035 / 41Cr4 Steel
Tensile strength: 980MPa
Yield point: 785MPa
Percentage reduction of area after fracture: 45%
Elongation after fracture: 9%
Impact test (+20°C): Transverse – 22J; Longitud – 30-35J
Quenched and Tempered (+QT) of W-Nr 1.7035 Steel
1. Heat din 1.7035 steel carefully to 850°C;
2. Soak at this temperature then quench in the oil;
3. Temper as soon as 41Cr4 steel reach room temperature (20°C);
4. Heat uniformly to the suitable temperature of 520°C;
5. Withdraw the material from the furnace and cool in the air.
Applications of DIN 41Cr4 Steel
After quenched and tempered,1.7035 steel can be used in the manufacture of medium speed,the load of parts,such as machine tools gear,shaft,worm,etc. Atfer QT and high-frequency surface hardening,41Cr4 steel is always used in the manufacture of high surface hardness,abrasion resistance parts. After quenching and middle temperature tempering,this material is usually used in the manufacture of overloading,medium speed impact of parts.
Enquiry for DIN 1.7035 / 41Cr4 Alloy Steel Round / Square / Flat Bars, Shafts, Rollers, Blocks.