1.2080 / X210Cr12
DIN 1.2080 / X210Cr12 Steel is a high Carbon and high Chromium cold work tool steel. The 1.2080 steel has good hardenability and wear resistance. But due to the carbon content of X210Cr12 steel is high,which makes this material hard and brittle. So din 1.2080 can not afford a bigger punch load and has low impact toughness.
C: 1.90-2.20; Si: 0.10-0.60; Mn: 0.20-0.60;
P: max0.030; S: max0.030; Cr: 11.00-13.00;
Form of 1.2080
Round / Flat Bars, Plates, Blocks
Size of X210Cr12
dia. 1-16mm (Cold Drawn);
dia. 10-50mm (Hot Rolled);
dia. 50-180mm (Hot Forged);
dia. 180-300mm (Free Forging);
Thickness: 1-2.5mm(Cold Rolled); 1.5-20mm(Hot Rolled); 20-300mm(Hot Forged);
Surface Condition of 1.2080 Steel
Black, Peeled, Rough Machined, Ground
Hardness of X210Cr12 Steel
Annealed (+A): 217-269HB
Mechanical Properties of W-Nr 1.2080 Steel
Percentage reduction of area after fracture
Elongation after fracture
Quenched and Tempered (+QT) of 1.2080 / X210Cr12
1. Heat din 1.2080 steel to the hardening temperature of 950-1000°C;
2. Quench in the oil then cool down;
3. Heat uniformly to the required tempering temperature;
4. Withdraw X210Cr12 steel from the furnace and cool in air;
5. The general tempering temperature is 200°C which can make the material at 60HRC.
Applications of DIN X210Cr12 Steel
The 1.2080 tool steel is usually used to make cold die that the impact load is small and with high wear resistance. X210Cr12 steel is also used for cold cutting blade,drill sets,gauge,drawing die,stamping die,thread rolling plate,deep drawing die and thread rolling die,etc.